PT-310 Petro tape
Product PT-310 Petro tape
PETRO TAPE is composed mainly of petrolatum, tannin, inert silica and special anti-corrosive agents, it will never evaporate, harden and its viscosity will never change. It will never crack or peel off.
Since it can perfectly adhere to any material and any complicated shape, the viscosity film formed on the applied surface prevents the penetration of moisture or air into the applied surface, it prevents all physical factors of corrosion.
Because the composition of PETRO TAPE is chemically stable, it will resist acids, alkali and salts. The anti-corrosive effect never changes with climate or temperature.
Features
- · Outstanding water and chemical resistance
- · Great efficiency with easy application
- · Non-cracking, non-hardening, non-hazardous, non-toxic
- · No changes in quality under extremely low temperature (-15°C)
- · Adheres well to rusty or slightly moist steel
- · Requires only hand or power tool cleaning
- · Encapsulates lead paints
Sub-Materials
- SHAIC Petro Paste
-
Primer for increasing adhesion and first layer for anti-corrosion which is applied before
petro tape wrapping without submerged parts.
- - Supply: 4 kg/can or 20 kg/can
- - Coverage: 300g/m²
- SHAIC Petro Mastic
- Filler for uneven surface such as flanges or valves which is applied before petro tape wrapping without sub-merged parts.
- - Supply: 500 g/each
- PVC FIRM TAPE
- Protection tape for wrapped Petro Tape from mechanical damages and for discrimination of oil, gas and water pipelines by different colors such as red, yellow, gray or blue, etc.
- - Size: 0.2mm Thickness X 50mm Width x 30m Length (Various Color & Width is available)
- MARINE PILING TAPE
- Corrosion protection tape on steel piles of the marine structure which can be applied without Petro Paste.
- - Size: 1.25mm Thickness X 50mm Width x 30m Length (Various Color & Width is available)
Physical Properties
| Product | Properties | Result | Test Method |
|---|---|---|---|
| SHAIC PETRO TAPE |
Thickness | 1.1mm | ASTM D1000 |
| Breaking Strength | 285N/50mm | ASTM D1000 | |
| Elongation | 25% | ASTM D1000 | |
| Breakdown Voltage | 13KV | ASTM D149 | |
| Resistance to Acids, Alkalies and Salts | Excellent | - | |
| Temperature Range | -20℃~80℃ | - | |
| SHAIC MARINE PILING TAPE |
Thickness | 1.25mm | ASTM D1000 |
| Breaking Strength | 285N/50mm | ASTM D1000 | |
| Elongation | 25% | ASTM D1000 | |
| Resistance to Acids, Alkalies and Salts | Excellent | - | |
| Temperature Range | -20℃~80℃ | - | |
| Breakdown Voltage | 13KV | ASTM D149 | |
| PETRO PASTE | Solid Content | 100% | - |
| Flash Point | 180℃ | ASTM D92 | |
| Specific Gravity | 1.25 | ASTM D70 | |
| Temperature Range | -25℃~50℃ | - | |
| SHAIC P.V.C FIRM TAPE |
Thickness | 0.2mm | ASTM D1000 |
| Breaking Strength | 39N/cm | ASTM D1000 | |
| Elongation | 290% | ASTM D1000 | |
| Adhesion to Steel | 2.6N/cm | ASTM D1000 | |
| Adhesion to Self | 2.1N/cm | ASTM D1000 | |
| Vapor Transmission | 0.19perms↓ | ASTM E96 | |
| Dielectric Strength | 13KV | ASTM D149 | |
| Insulation Resistance (MΩ·cm) | 106↑ | ASTM D257 |
Simple Application
- · Remove rust with wire-brush and wipe soil with rags.
- · Apply a uniform & thin layer of Petro Paste by gloved hand to displace any moisture if remained.
Drying or curing time is not required and application of Petro Tape may begin immediately. - · Apply Petro Mastic on complicated and uneven surface such as valve and flange to fill or smooth the voids, if needed.
- · Wrap Petro Tape spirally around surface or apply precut pieces over irregular surfaces with a minimum 25mm overlap or with a 50% overlap for optimum results. Conform and seal edges of tape using hands with rubber gloves to give monolithic appearance.
- · PVC Firm Tape is used in place where finishing. Wrap PVC Firm Tape spirally or precut as needed.
25mm minimum overlap is required.